The sintering behaviour of several ceramics prepared using a previously selected mixture of incinerated paper mill sludge and glass cullet which was blended with 10, 20, 30 and 40 wt% of some natural clayey materials has been studied. Three natural commercial product were used: a red clay, a yellow clay and a kaolin. Mixtures were blended by wet attrition milling, dried, sieved, pressed into specimens and then fired for 1 h at temperatures ranging from 1040 to 1140 °C. The resulting materials were characterized by water absorption, shrinkage and crystallographic composition. It was observed that materials containing kaolin display the best overall behaviour independently of the quantity of kaolin introduced. Conversely the optimal sintering temperature, and consequently the best properties of materials prepared using red or yellow clay was found above 1080 °C and depends of their specific composition being affected by the amount of clay added.

Sintering behaviour of ceramics containing paper sludge, glass cullet and different types of clayey materials

FURLANI, Erika;TONELLO, Gabriele;MASCHIO, Stefano;ANEGGI, Eleonora;MINICHELLI, Dino;BRUCKNER, Sergio;
2010-01-01

Abstract

The sintering behaviour of several ceramics prepared using a previously selected mixture of incinerated paper mill sludge and glass cullet which was blended with 10, 20, 30 and 40 wt% of some natural clayey materials has been studied. Three natural commercial product were used: a red clay, a yellow clay and a kaolin. Mixtures were blended by wet attrition milling, dried, sieved, pressed into specimens and then fired for 1 h at temperatures ranging from 1040 to 1140 °C. The resulting materials were characterized by water absorption, shrinkage and crystallographic composition. It was observed that materials containing kaolin display the best overall behaviour independently of the quantity of kaolin introduced. Conversely the optimal sintering temperature, and consequently the best properties of materials prepared using red or yellow clay was found above 1080 °C and depends of their specific composition being affected by the amount of clay added.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11390/881731
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact