An experimental investigation is presented regarding the compressive and shear strength of monolithic and PVB laminated glass elements connected by acrylic glue. Ultrasonic tests were also used to control the efficiency of glued surfaces of glass panels. Twenty-four triplets composed of three float glass elements glued with acrylic adhesive were prepared to perform bond tests. Of these twelve triplets were made with monolithic glass elements with a nominal thickness of 20 mm, while twelve were made with layered glass elements 20 mm thick. Three single elements of monolithic glass and three of layered glass were tested for compressive strength. Ultrasonic tests were performed on a sample made by gluing two layered glass panels 200 × 300 × 20 mm in thickness in which defects in glued surfaces were generated artificially. Experimental stress-strain curves in compression for glass elements and shear stress-slippage curves from bond tests were also derived with crack patterns at rupture.

Bond characterization of monolithic and layered glass panels and ultrasonic tests to control glued surfaces

PAULETTA M
2019-01-01

Abstract

An experimental investigation is presented regarding the compressive and shear strength of monolithic and PVB laminated glass elements connected by acrylic glue. Ultrasonic tests were also used to control the efficiency of glued surfaces of glass panels. Twenty-four triplets composed of three float glass elements glued with acrylic adhesive were prepared to perform bond tests. Of these twelve triplets were made with monolithic glass elements with a nominal thickness of 20 mm, while twelve were made with layered glass elements 20 mm thick. Three single elements of monolithic glass and three of layered glass were tested for compressive strength. Ultrasonic tests were performed on a sample made by gluing two layered glass panels 200 × 300 × 20 mm in thickness in which defects in glued surfaces were generated artificially. Experimental stress-strain curves in compression for glass elements and shear stress-slippage curves from bond tests were also derived with crack patterns at rupture.
File in questo prodotto:
File Dimensione Formato  
Bond characterization of monolithic and layered glass panels and ultrasonictests to control glued surfaces.pdf

non disponibili

Descrizione: PDF della versione pubblicata
Tipologia: Versione Editoriale (PDF)
Licenza: Non pubblico
Dimensione 2.25 MB
Formato Adobe PDF
2.25 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11390/1176751
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 9
  • ???jsp.display-item.citation.isi??? 5
social impact