Investigation of the Failure Modes of Textile-Reinforced Concrete and Fiber/Textile-Reinforced Concrete under Uniaxial Tensile Tests

Recently, innovations in textile-reinforced concrete (TRC), such as the use of basalt textile fabrics, the use of high-performance concrete (HPC) matrices, and the admixture of short fibers in a cementitious matrix, have led to a new material called fiber/textile-reinforced concrete (F/TRC), which represents a promising solution for TRC. Although these materials are used in retrofit applications, experimental investigations about the performance of basalt and carbon TRC and F/TRC with HPC matrices number, to the best of the authors’ knowledge, only a few. Therefore, an experimental investigation was conducted on 24 specimens tested under the uniaxial tensile, in which the main variables studied were the use of HPC matrices, different materials of textile fabric (basalt and carbon), the presence or absence of short steel fibers, and the overlap length of the textile fabric. From the test results, it can be seen that the mode of failure of the specimens is mainly governed by the type of textile fabric. Carbon-retrofitted specimens showed higher post-elastic displacement compared with those retrofitted with basalt textile fabrics. Short steel fibers mainly affected the load level of first cracking and ultimate tensile strength.