Copper and manganese additives for pressureless sintering of Ce-TZP have been studied, the former because its atomic radius is close to that of Ce4+, the latter because its atomic radius is close to that of Zr4+. The temperature at which shrinkage begins did not decrease when using CuO or MnO2, but at a given temperature, the sintering rate was higher. CuO and MnO2 were also very effective in improving both the tetragonal phase content retained at room temperature and the mechanical properties (hardness, bending strength and toughness).

SINTERING AIDS FOR CERIA ZIRCONIA ALLOYS

MASCHIO, Stefano;
1992-01-01

Abstract

Copper and manganese additives for pressureless sintering of Ce-TZP have been studied, the former because its atomic radius is close to that of Ce4+, the latter because its atomic radius is close to that of Zr4+. The temperature at which shrinkage begins did not decrease when using CuO or MnO2, but at a given temperature, the sintering rate was higher. CuO and MnO2 were also very effective in improving both the tetragonal phase content retained at room temperature and the mechanical properties (hardness, bending strength and toughness).
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11390/681866
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 12
  • ???jsp.display-item.citation.isi??? 11
social impact