Thermodilatometric tests have been performed to investigate the shrinkage of green compacts of pure and ZnO-doped 4ZrO2-5TiO2 SnO2 prepared by dry ball milling, flo-deflocculation and coprecipitation. Experiments have shown that the powder preparation procedure has a significant influence on the sintering process. Optimizing the homogeneity composition, which is enhanced from dry ball milling to coprecipitation, raises the starting sintering temperature. The reduction of the dimension of the starting particles increases the sintering rate and the addition of ZnO favours the shrinkage of the green bodies. Coprecipitated products lead to the highest final density because the evaporation of tin oxide on firing is reduced.

THERMODILATOMETRIC BEHAVIOR OF PURE AND DOPED ZRTIO4-SNO2

MASCHIO, Stefano;
1994

Abstract

Thermodilatometric tests have been performed to investigate the shrinkage of green compacts of pure and ZnO-doped 4ZrO2-5TiO2 SnO2 prepared by dry ball milling, flo-deflocculation and coprecipitation. Experiments have shown that the powder preparation procedure has a significant influence on the sintering process. Optimizing the homogeneity composition, which is enhanced from dry ball milling to coprecipitation, raises the starting sintering temperature. The reduction of the dimension of the starting particles increases the sintering rate and the addition of ZnO favours the shrinkage of the green bodies. Coprecipitated products lead to the highest final density because the evaporation of tin oxide on firing is reduced.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11390/686347
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 5
  • ???jsp.display-item.citation.isi??? 5
social impact