he effect of support material on the catalytic performance for methane combustion has been studied for bimetallic palladium-platinum catalysts and compared with a monometallic palladium catalyst on alumina. The catalytic activities of the various catalysts were measured in a tubular reactor, in which both the activity and stability of methane conversion were monitored. In addition, all catalysts were analysed by temperature-programmed oxidation and in situ XRD operating at high temperatures in order to study the oxidation/reduction properties. The activity of the monometallic palladium catalyst decreases under steady-state conditions, even at a temperature as low as 470 degrees C. In situ XRD results showed that no decomposition of bulk PdO into metallic palladium occurred at temperatures below 800 degrees C. Hence, the reason for the drop in activity is probably not connected to the bulk PdO decomposition. All Pd-Pt catalysts, independently of the support, have considerably more stable methane conversion than the monometallic palladium catalyst. However. dissimilanties in activity and ability to reoxidise PdO were observed for the various support materials. Pd-Pt supported on Al2O3 was the most active catalyst in the low-temperature region, Pd-Pt supported on ceria-stabilised ZrO2 was the most active between 620 and 800 degrees C, whereas Pd-Pt supported on LaMnAl11O19 was superior for temperatures above 800 degrees C. The ability to reoxidise metallic Pd into PdO was observed to vary between the supports. The alumina sample showed a very slow reoxidation, whereas ceria-stabilised ZrO2 was clearly faster.

Catalytic combustion of methane over bimetallic Pd-Pt catalysts: the influence of support materials

COLUSSI, Sara;TROVARELLI, Alessandro;
2006

Abstract

he effect of support material on the catalytic performance for methane combustion has been studied for bimetallic palladium-platinum catalysts and compared with a monometallic palladium catalyst on alumina. The catalytic activities of the various catalysts were measured in a tubular reactor, in which both the activity and stability of methane conversion were monitored. In addition, all catalysts were analysed by temperature-programmed oxidation and in situ XRD operating at high temperatures in order to study the oxidation/reduction properties. The activity of the monometallic palladium catalyst decreases under steady-state conditions, even at a temperature as low as 470 degrees C. In situ XRD results showed that no decomposition of bulk PdO into metallic palladium occurred at temperatures below 800 degrees C. Hence, the reason for the drop in activity is probably not connected to the bulk PdO decomposition. All Pd-Pt catalysts, independently of the support, have considerably more stable methane conversion than the monometallic palladium catalyst. However. dissimilanties in activity and ability to reoxidise PdO were observed for the various support materials. Pd-Pt supported on Al2O3 was the most active catalyst in the low-temperature region, Pd-Pt supported on ceria-stabilised ZrO2 was the most active between 620 and 800 degrees C, whereas Pd-Pt supported on LaMnAl11O19 was superior for temperatures above 800 degrees C. The ability to reoxidise metallic Pd into PdO was observed to vary between the supports. The alumina sample showed a very slow reoxidation, whereas ceria-stabilised ZrO2 was clearly faster.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11390/691104
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 79
  • ???jsp.display-item.citation.isi??? 77
social impact